Two novel techniques were developed to fabricate robust, low-defect films of 3D-ordered polystyrene latexes with titania shell. One is sonication-assisted casting that was used to prepare highly ordered three dimensional (3D) latex films of centimeter sizes from aqueous polystyrene microspheres of different diameters (202-1053 nm). The thickness of the 3D-ordered latex film was adjustable from several layers to several tens of layers by changing the concentration of the latex solution The films showed photonic stop bands according to the sphere size in the as-prepared 3D-ordered latex film. The other novel technique, i.e., a gas-phase surface sol-gel process (G-SSG), was used to coat the surface of the spheres with a nm-thick titania layer without dipping. This procedure glued the spheres together to give mech. more robust films without changing its morphol. These 3D-ordered latex films, both as-prepared and titania coated, displayed photonic stop bands that are consistent with theor. estimates based on the latex size.